LEXAN&tade; HPS1 esin聚碳酸酯SABIC Innovative Plastics产品说明:High flow polycabonate. Fo medical devices and phamaceutical applications. Healthcae management of change, biocompatible (ISO10993 o USP Class VI). EtO, e-beam and gamma steilizable. Co
ntains mold elease.
单位:
公制|
英制- Popeties
- 加工方式
- 资料
- 视觉搜索
- 曲线数据
- 购买地点
总体材料状态资料1搜索 UL 黄卡- SABIC Innovative Plastics
供货地区添加剂特性用途机构评级加工方法物理性能额定值单位制测试方法
比重--1.20
ASTM D792--1.20g/cm3
ISO 1183--1.19g/cm3
ASTM D792特定体积23.1in3/lb
ASTM D792熔流率（熔体流动速率）(300°C/1.2 kg)25g/10 min
ASTM D1238溶化体积流率（MVR）(300°C/1.2 kg)1.40in3/10min
ISO 1133收缩率 - 流动(0.126 in)5.0E-3 到 7.0E-3in/in
内部方法吸水率ASTM D57024 h0.15%
平衡, 73°F0.35%
平衡, 212°F0.58%
硬度额定值单位制测试方法
洛氏硬度ASTM D785M 级70
R 级118
球压硬度(H 358/30)13800psi
ISO 2039-1机械性能额定值单位制测试方法
拉伸模量--2345000psi
ASTM D638--341000psi
ISO 527-2/1抗张强度屈服39000psi
ASTM D638屈服9140psi
ISO 527-2/50断裂39500psi
ASTM D638断裂7250psi
ISO 527-2/50伸长率屈服36.0%
ASTM D638屈服6.0%
ISO 527-2/50断裂3120%
ASTM D638断裂70%
ISO 527-2/50弯曲模量1.97 in 跨距4335000psi
ASTM D790--5334000psi
ISO 178弯曲应力--5,613100psi
ISO 178屈服, 1.97 in 跨距413500psi
ASTM D790泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮)10.0mg
ASTM D1044冲击性能额定值单位制测试方法
简支梁缺口冲击强度7ISO 179/1eA-22°F4.8ft·lb/in2
73°F5.7ft·lb/in2
悬壁梁缺口冲击强度Colos2.0 到 12ft·lb/in
ASTM D256Natual, Tints12ft·lb/in
ASTM D256-22°F84.8ft·lb/in2
ISO 180/1A73°F85.7ft·lb/in2
ISO 180/1A无缺口悬臂梁冲击73°F60ft·lb/in
ASTM D4812-22°F8无断裂
ISO 180/1U73°F8无断裂
ISO 180/1U装有测量仪表的落镖冲击(73°F, Enegy at Peak Load)480in·lb
ASTM D3763落锤冲击(73°F)1500in·lb
ASTM D3029拉伸冲击强度9180ft·lb/in2
ASTM D1822热性能额定值单位制测试方法
载荷下热变形温度66 psi, 未退火, 0.252 in280°F
ASTM D64866 psi, 未退火, 3.94 in 跨距10271°F
ISO 75-2/Be264 psi, 未退火, 0.252 in260°F
ASTM D648264 psi, 未退火, 3.94 in 跨距10250°F
ISO 75-2/Ae维卡软化温度--282°F
ISO 306/B50--284°F
ISO 306/B120Ball Pessue Test(257°F)通过
IEC 60695-10-2线形热膨胀系数 - 流动-40 到 203°F3.8E-5in/in/°F
ASTM E83173 到 176°F3.9E-5in/in/°F
ISO 11359-2比热0.300Btu/lb/°F
ASTM C351导热系数--1.3Btu·in/h/ft2/°F
ASTM C177--1.4Btu·in/h/ft2/°F
ISO 8302电气性能额定值单位制测试方法
表面电阻率> 1.0E+15ohms
IEC 60093体积电阻率--> 1.0E+17ohms·cm
ASTM D257--> 1.0E+15ohms·cm
IEC 60093介电强度0.126 in, in Ai380V/mil
ASTM D1490.126 in, 在油中430V/mil
IEC 60243-1介电常数50 Hz3.17
ASTM D15060 Hz3.17
ASTM D1501 MHz2.96
ASTM D15050 Hz2.70
IEC 6025060 Hz2.70
IEC 602501 MHz2.70
IEC 60250耗散因数50 Hz9.0E-4
ASTM D15060 Hz9.0E-4
ASTM D1501 MHz0.010
ASTM D150,
IEC 6025050 Hz1.0E-3
IEC 6025060 Hz1.0E-3
IEC 60250可燃性额定值单位制测试方法
极限氧指数25%
ISO 4589-2光学性能额定值单位制测试方法
折射率1.586
ASTM D542透射率(100 mil)88.0%
ASTM D1003雾度(100 mil)1.0%
ASTM D1003注射额定值单位制
干燥温度250°F
干燥时间3.0 到 4.0h
干燥时间，最大48h
建议的最大水分含量0.020%
建议注射量40 到 60%
料筒后部温度480 到 520°F
料筒中部温度500 到 540°F
料筒前部温度520 到 560°F
射嘴温度510 到 550°F
加工（熔体）温度520 到 560°F
模具温度160 到 200°F
背压50.0 到 100psi
螺杆转速40 到 70pm
排气孔深度1.0E-3 到 3.0E-3in